Effect of an abrupt change in pulling rate on microstructures of directionally solidified Al2O3-Er3Al5O12 eutectic and off-eutectic composite ceramics

Directionally solidified microstructures of Al₂O₃-Er₃Al₅O₁₂ eutectic and off-eutectic in situ composite ceramics were explored under abrupt-change pulling rate conditions. Corresponding temperature distributions and interface locations were studied. In eutectic composition, fluctuation of eutectic spacing occurred when the pulling rate increased abruptly. A gradually increase or abrupt increase in eutectic spacing was observed when the pulling rate decreased abruptly. In hypoeutectic and hypereutectic compositions, formation of the primary phases were suppressed when the pulling rate increased abruptly from 10?µm/s to 100?µm/s, while primary phases precipitated when the pulling rate decreased abruptly from 100?µm/s to 10?µm/s. The interface altitude decreased after the pulling rate increased abruptly, but increased after the pulling rate decreased abruptly. The liquid composition restriction (around the eutectic composition) at the eutectic interface plays an important role in the suppression of the primary dendrite and coupled eutectic oxides can be obtained in off-eutectic compositions even under higher solidification rate conditions.     

A method for rapidly evaluating reliability and predicting remaining useful life using two-dimensional convolutional neural network with signal conversion

Journal of Mechanical Science and Technology - Real-time monitoring and rapid evaluation of bearing operating conditions, especially for the reliability evaluation and remaining useful life (RUL)...     

焊缝表面缺陷激光扫描三维重构测量

为检测工件焊缝表面缺陷，采用点激光位移传感测距法和数据拟合技术进行焊缝表面缺陷检测试验研究. 首先采集缺陷表面轮廓数据点，利用高斯滤波对原始数据降噪处理. 再对处理后的数据点进行Delaunay三角剖分，使散乱点连接并结合其空间坐标重构出缺陷的三维模型. 结果表明，基于点激光位移传感测距技术及焊缝表面缺陷三维重构方法可以准确判断焊缝成形情况.     

Semantic word shifts in a scientific domain

Understanding semantic word shifts in scientific domains is essential for facilitating interdisciplinary communication. Using a data set of published papers in the field of information retrieval (IR), this paper studies the semantic shifts of words in IR based on mining per-word topic distribution over time. We propose that semantic word shifts not only occur over time, but also over topics. The shifts are examined from two perspectives, the topic-level and the context-level. According to the over-time word-topic distribution, stable words and unstable words are recognized. The diverging and converging trends in the unstable type reveal characteristics of the topic evolution process. The context-level shifts are further detected by similarities between word vectors. Our work associates semantic word shifts with the evolving of topics, which facilitates a better understanding of semantic word shifts from both topics and contexts.     

古建筑木结构透榫节点力学模型研究

为研究古建筑木结构透榫节点的M-θ力学模型，在分析透榫节点构造特征与受力机理的基础上，建立其数值模型，用透榫节点的试验数据验证了该数值模型的正确性，并分析了节点缝隙、木材横纹弹性模量和大榫头长度对透榫节点受弯承载力的影响。根据受力分析结果，建立以弹性点、屈服点与极限点为特征点的三折线多参数M-θ力学模型，其结果与多数的试验结果基本吻合，并将该力学模型应用于木构架的受力分析。研究结果表明：透榫节点的滞回耗能能力强，节点的变形主要集中在榫头处。当榫头与卯口之间的缝隙增大时，节点的受弯承载力降低。随木材横纹弹性模量的提高和大榫头长度的增加，节点的受弯承载力有一定提高。文章建立的M-θ力学模型能较好反映透榫节点的受力过程，适用于木构架的受力分析，其荷载 位移骨架曲线与试验结果基本吻合。研究成果可为古建筑木结构的维修与保护提供参考。     

基于改进人工蜂群算法的多目标绿色柔性作业车间调度研究

针对多目标绿色柔性作业车间调度问题（MGFJSP）的特点，提出从碳排放量、噪声和废弃物这3个指标来综合评定环境污染程度，建立了以最小化最大完成时间和环境污染程度为优化目标的MGFJSP模型，并提出了一种改进的人工蜂群算法来求解该模型。算法的具体改进包括：设计了一种三维向量的编码和对应解码方案，在跟随蜂搜索阶段引入一种有效的动态邻域搜索操作来提高算法的局部搜索能力，在侦查蜂阶段提出产生新食物源的策略用于增加种群的多样性。最后进行了实验研究与算法对比，以验证所建模型和所提算法的有效性。     

基于步冷试验的2.25Cr-1Mo-0.25V钢母材及焊缝回火脆化研究

对原始态、步冷态、脱脆态和脱脆步冷态2.25Cr-1Mo-0.25V钢母材及焊缝冲击试验结果进行分析,得到了母材和焊缝在不同状态下的韧脆转变温度vTr54.2和FATT以及脆化度ΔvTr54.2和ΔFATT。试验结果表明,步冷试验之后,母材发生较低程度脆化或脱脆现象,但是脆化度或脱脆度较低,表明母材具有良好的抗回火脆化性能;经脱脆试验后,母材和焊缝都发生较高程度的脱脆,表明材料的脆化主要是由于回火脆化引起的,脱脆试验使得材料的韧脆转变温度降低;脱脆步冷试验后,焊缝发生较高程度的脆化,焊缝对脱脆步冷试验的敏感性较高,脱脆步冷试验有效促进了焊缝的脆化。在相同脆化条件下,母材的脆化敏感性低于焊缝,焊缝更易发生脆化。